Mylar Glass Transition Data Sheet

How to measure glass transition temperature the most usual test method to determine glass transition temperature of plastics is astm e1356.

Mylar glass transition data sheet.

Mylar can be aluminized by evaporating a thin film of metal onto it to reduce its permeability. Mylar polyester film is a flexible strong and durable film with an unusual balance of properties making it suitable for many industrial applications. Vicat softening point astm d1525. To see matweb s complete data sheet for this material including material property data.

Mylar is 1 7 10 5 in in c 9 5 10 6 in in f. Glass transition temperature c 78 121 375 performance improvement shrinkage 150 c after 30 minutes 1 5 0 4 18 performance improvement typical coefficient of thermal expansion ppm c 22 5 19 0 200 performance improvement 1 3 modulus of elasticity gpa 150 c. Multiplying the indicated change by the sample length gives the thermal dimensional change in the sheet of mylar. Mylar a 12 36μm.

As a guide to estimating changes due to thermal expansion figure 5 gives the dimensional changes in in over a wide temperature range. Type mylar a is a tough general purpose film which is transparent in 12μm through 23μm and translucent in heavier thickness. Data sheet 48 f 1m metallized pet close window cs hyde company stocks and converts different types of polyester film dupont mylar type a off white standard industry grade electronics grade type el optically clear and metallic metalized polyester film. Color conferring dyes can easily be formulated into pet sheet.

This page displays only the text of a material data sheet. Crystallization of bpf epoxy resins is possible in the temperature range between the glass transition point 10 to 20 c 14 to 4 f and the general melting range typically 30 to 60 c 86 to 140 f. This test method covers the assignment of the glass transition temperatures of materials using differential scanning calorimetry or differential thermal analysis. Peel strength astm d 1876 72 mylar film.

This data sheet also covers the following dupont teijin films which are not branded as mylar products. Ac dielectric strength typical value for mylar 92 el c 25 c 77 f 7 0 kv mil astm d149 and astm d2305 60 hz 500 v sec rate of rise gauge and type at 25 c 77 f minimum values for mylar el film 48el 2 8 kv astm d149 and d2305 75el 3 5 kv minimum average 92el 4 0 kv voltage of 10 sheet 142el 5 5 kv samples 200el 7 7 kv 300el 10 0 kv 60 hz. When filled with glass particles or fibres. Glass transition temp tg dsc.